分子筛
物品单位 品牌
zzstandard
  • 产地:国外
  • 货号:MS-10010
  • 发布日期: 2020-07-22
  • 更新日期: 2022-04-26
产品详细说明
产地 国外
品牌 zzstandard
货号 MS-10010
用途范围 咨询甄准
纯度 咨询甄准%
CAS编号
规格 5g
是否进口
品牌产品编号品名参数
甄准MS-10010KIT-6孔径:7-8 nm, SSA大于 600/g  
进口原装MS-20010KIT-6Preparation Method: Hydrothermal Method ; BET Surface Area (m2;g)  600-800 ; Comparative Crystallinity (%)  90 ; Total Adsorption Average Pore Width (nm)  4.3 ; BJH Adsorption Average Pore Width (nm)  6.2 ; Phase  Cubic Ia3d Silica ; Particle Size  10 - 100μm
甄准MS-10020MCM-41BET比表面积 m2/g: 800; 相对结晶度%: 90; Na2O%: 0.05; 灼减%: 5; 孔径nm: 3-5
进口原装MS-20020MCM-41Grade: Reagent grade; Linear Formula: SiO2 (pure Sio2); Appearance: White Powder
Average Pore Diameter: 3.4nm; Particle Size: 100nm - 1000nm; BET surface area(m2/g):>850; Pore Volume(cm3/g):>0.75; Na2O:<0.5%
进口原装MS-20030MCM-41Grade: Industrial grade; Linear Formula: SiO2 (pure Sio2); Appearance: White Powder
Average Pore Diameter: 3.5nm-4.0nm; Particle Size: 200nm - 1000nm; BET surface area(m2/g):>800; Pore Volume(cm3/g):>0.75; Na2O:<0.5%
甄准MS-10030SBA-15孔径 : 6-10 nm; BET比表面积:  550-600 m2/g; 相对结晶度:  90%; SiO2/Al2O3 500mol  纯硅; Na2O 0.1%; 灼减 5%  
进口原装MS-20040SBA-15Preparation Method: Hydrothermal Method; BET surface area (m2/g): ~600
Average Pore Diameter (nm): 7~10; Particle Size: 1~2μm; Phase: p6mm; Na2O (%): 0.1; Comparative Crystallinity (%)  90; BJH Desorption Cumulative Volume of Pores (cm3/g): 0.6793
进口原装MS-20050SBA-16Preparation Method  Hydrothermal Method; BET Surface Area (m2/g)  700-900; Average Pore Diameter (nm)  3-5; BJH Desorption Cumulative Volume of Pores (cm3/g)  0.9772; Phase  Im3m
甄准MS-10040TS-1粒径:800nm; 比表面积:350-450; 孔径:0.56-0.58nm; 结晶度:>95%; Na2O<0.1wt%; Si/Ti~30
进口原装MS-20060TS-1Titanium Silicalite-1; BET surface area (m2/g):  360-420; Pore Size (nm):  0.56-0.58; Comparative Crystallinity (%):  >95; Na2O (wt.%):  <0.1; Si/Ti:  ~30; Cation:  H
甄准MS-10050SAPO-34形态:白色粉末; 比表面积:≥550 m2/g; 孔容:≥0.27 cm3/g; 氧化硅含量: ~10%; 氧化铝含量: ~42%; 氧化钠含量:≤0.1%
进口原装MS-20070SAPO-34Appearance: White Powder; Specific Surface Area (m2/g) 550; Pore Volume (cm3/g) 0.27; Average Particle Size (μm)  ~2; SiO2 (%)~10; Al2O3 (%)~42; Na2O(%) 0.1; Cation  H
甄准MS-10060SAPO-11比表面积:≥180/g; 孔体积: 0.27/g; 孔容:≥0.0.16cm3/g; 氧化硅含量: ~6%; 氧化铝含量: ~48%; 氧化钠含量:≤0.2%
进口原装MS-20080SAPO-11Appearance White Powder; Specific Surface Area (m2/g)180; Pore Volume (cm3/g)0.16; SiO2(%) ~6; Al2O3 (%) ~48; Na2O (%) 0.2
甄准MS-10070ZSM-5硅铝比SiO2/Al2O3:38,孔径:0.53~0.58 nm
甄准MS-10071ZSM-5硅铝比SiO2/Al2O3:70,孔径:0.53~0.58 nm
甄准MS-10072ZSM-5硅铝比SiO2/Al2O3:170,孔径:0.53~0.58 nm
甄准MS-10073ZSM-5硅铝比SiO2/Al2O3:350-400,孔径:0.53~0.58 nm
甄准MS-10074ZSM-5硅铝比SiO2/Al2O3:500,孔径:0.53~0.58 nm,<, SPAN style="mso-spacerun: yes">  
进口原装MS-20090Nano ZSM-5(氢型)SiO2/Al2O3 Molar Ratio: 26; Na: <0.1%; Crystal Size(nm): 300; H2O(%wt): <5; BET (m2/g): 362; Relative Crystallization: 100%; Shape: Sphere; Pore Size: ~5A
进口原装MS-20091Nano ZSM-5(氢型)SiO2/Al2O3 Molar Ratio: 52; Na: <0.1%; Crystal Size(nm): 300; H2O(%wt): <5; BET (m2/g): 362; Relative Crystallization: 98%; Shape: Sphere; Pore Size: ~5A
进口原装MS-20092Nano ZSM-5(氢型)SiO2/Al2O3 Molar Ratio: 87; Na: <0.1%; Crystal Size(nm): 300; H2O(%wt): <5; BET (m2/g): 362; Relative Crystallization: 100%; Shape: Sphere; Pore Size: ~5A
进口原装MS-20093Nano ZSM-5(氢型)SiO2/Al2O3 Molar Ratio: 91; Na: <0.1%; Crystal Size(nm): 300; H2O(%wt): <5; BET; m2/g): 362; Relative Crystallization: 99%; Shape: Sphere; Pore Size: ~5A
进口原装MS-20094Nano ZSM-5(氢型)SiO2/Al2O3 Molar Ratio: 371; Na: <0.1%; Crystal Size(nm): 300? 700; H2O(%wt): <5; BET (m2/g): 362; Relative Crystallization: 100%; Shape: Rod; Pore Size: ~5A
进口原装MS-20100ZSM-5 Series Zeolite Powder,(氢型)(钠型)Preparation Method: Hydrothermal Method; Linear Formula: (SiO2)x(Al2O3)y; Pore Size: ~5A; SiO2/Al2O3 Molar Ratio: 38; Average Particle Size: 2μm; BET Surface Area m2/g: >380; Na2O: <0.2; Adsorption: 9.5
进口原装MS-20101ZSM-5 Series Zeolite Powder(氢型)Preparation Method: Hydrothermal Method; Linear Formula: (SiO2)x(Al2O3)y; Pore Size: ~5A; SiO2/Al2O3 Molar Ratio: 117; Average Particle Size: 2μm; BET Surface Area m2/g: >380; Na2O: <0.2; Adsorption: 9.5
进口原装MS-20102ZSM-5 Series Zeolite Powder(氢型)Preparation Method: Hydrothermal Method; Linear Formula: (SiO2)x(Al2O3)y; Pore Size: ~5A; SiO2/Al2O3 Molar Ratio:   360; Average Particle Size: 2μm; BET Surface Area m2/g: >380; Na2O: <0.1; Adsorption: 9.5
进口原装MS-20110ZSM-5 Adsorbent SeriesZSM-5 Adsorbent: Hydrophobic Zeolite Adsorbent; Preparation Method  Hydrothermal Method; SiO2/Al2O3 Molar Ratio  300; BET Surface Area (m2/g)  220; Bulk Density (g/ml)  ~0.68; Na2O (%)  0.2; Comparative Crystallinity (%)  90; Adsorption of Hexane W%  7.2; Adsorption of Water W%  2; Compressive Strength (N/mm2)  25; Shape  Granular D:2-3.0mm; Pore Size  ~5A
进口原装MS-20111ZSM-5 Adsorbent SeriesZSM-5 Adsorbent: Binder-free Hydrophobic Zeolite Adsorbent; Preparation Method  Hydrothermal Method; SiO2/Al2O3 Molar Ratio  300; BET Surface Area (m2/g)  220; Bulk Density (g/ml)  ~0.68; Na2O (%)  0.2; Comparative Crystallinity (%)  90; Adsorption of Hexane W%  7.2; Adsorption of Water W%  2; Compressive Strength (N/mm2)  25; Shape  Granular D:2-3.0mm; Pore Size  ~5A